Silicone resins offered by Athon are materials with different degrees of crosslinking, obtained from mono- (M), di- (D), tri- (T) and tetra-functional (Q) monomers. The presence of different organic groups, mainly methyl and phenyl, give the resins superior release properties, temperature resistance, film formation and other characteristics that make these materials extremely important in the formulation of special release agents and high temperature coatings, among other applications.
Athon MQ 893 Resin is a silicone resin dispersed in polydimethylsiloxane fluid, formulated for high release efficiency.
•Good heat stability
•Water repellency superior to common silicone fluids
•Provides mold release and shine to formulations
Athon MQ 893 Resin is usually diluted with solvent (1 part product to 10 parts solvent) prior to brushing or by spraying onto the mold. Suitable solvents: aliphatic, aromatic or chlorinated hydrocarbons.
Also used in product formulations for HomeCare and AutoCare, providing shine and fixation by film formation.
Release agent
Household
Autocare
Household & Autocare
Industrial Release Agents
Canister 20L
Drum 200L
IBC 1.000L
Athon MQ 885 Resin is a non-flammable hydrotreated hydrocarbon silicone resin solution used in the formulation of mold releases and water repellants.
•Good heat stability
•Water repellency superior to common silicone fluids
•Provides mold release and shine to formulations
Athon MQ 885 Resin is usually diluted with solvent (1 part product to 10 parts solvent) prior to brushing or by spraying onto the mold. Suitable solvents: aliphatic, aromatic or chlorinated hydrocarbons.
Also used in product formulations for HomeCare and AutoCare, providing shine and fixation by film formation, as well as premium water repellency.
Release agent
Household
Autocare
Industrial Textile
Industrial Release Agents
Canister 20L
Drum 200L
IBC 1.000L
Athon MQ 835 Resin is a silicone resin dispersed in polydimethylsiloxane fluid, formulated for high release efficiency.
•Good heat stability
•Leaves no residue on metal molds
•Good wetting and spreading in molds
•Less need to clean molded parts before finishing
Athon MQ 835 Resin is usually diluted with solvent (1 part product to 10 parts solvent) prior to brushing or by spraying onto the mold. Suitable solvents: aliphatic, aromatic or chlorinated hydrocarbons.
Also used in product formulations for HomeCare and AutoCare, providing shine and fixation by film formation.
Release agent
Household
Autocare
Household & Autocare
Industrial Release Agents
Canister 20L
Drum 200L
IBC 1.000L
Athon MQ 830 Resin is a silicone resin dispersed in cyclosiloxane fluid, formulated for high release efficiency.
•Good heat stability
•Does not leave residues in metal molds
•Good wetting and spreading in molds
•Less need to clean molded parts before finishing
•Drying with film formation
Athon MQ 830 Resin is used as a release agent normally diluted with solvent prior to application by brushing or spraying into the mold. Suitable solvents: aliphatic, aromatic or chlorinated hydrocarbons.Úlso used in product formulations for HomeCare and AutoCare, providing shine and fixation by film formation.
Release agent
Household
Autocare
Industrial Release Agents
Canister 20L
Drum 200L
IBC 1.000L
Athon MQ 800 Resin is a powdered silicone resin used in formulation of release agents and products that require shine and fixation.
•Good heat stability
•Does not leave residues in metal molds
•Good wetting and spreading in molds
•Less need to clean molded parts before finishing
•Drying with film formation
Athon MQ 800 Resin is used as a release agent normally diluted with solvent prior to application by brushing or spraying into the mold. Suitable solvents: aliphatic, aromatic or chlorinated hydrocarbons.
Also used in product formulations for HomeCare and AutoCare, providing shine and fixation by film formation.
Release agent
Household
Autocare
Industrial Release Agents
Canister 20L
Drum 200L
IBC 1.000L
Athon MP 880 Resin is a solution of methylphenyl silicone resin in xylene.
•Good storage stability when mixed with zinc powder and aluminum pigments
•Easy to use
•Heat stability up to 650°C in combination with aluminum or micaceous iron pigments
Applicable to all types of heat resistant paints. It is the material of choice for anticorrosive coatings in engine parts, furnaces, chimneys, exhaust systems, boilers, ovens and oven parts, grills, electric and gas heaters, incinerators.
For temperatures above 250°C, the organic groups of silicone resins begin to degrade. After all silicone resin organic components have pyrolytically degraded, the remaining product changes to an inorganic stoichiometric composition of (SiO2)n. It is this layer that securely adheres the pigments and fillers to the coated substrate.
Any heat-stable inorganic pigments may be used:
•White, silver, black and colored ones
•Aluminum pigments provide the best heat resistance, up to 600°C
•Black pigments up to 500°C
•Mica and talc can be used as fillers
Recommendations for proper use:
• It is necessary to ensure adequate dispersion of pigments and fillers in the paint
• Sandblasting and degreasing of the substrate are recommended
• The paint can be made by spraying, immersion or brushing
• The product dries completely at room temperature, promoting temporary protection against corrosion
• The optimum mechanical properties and oil resistance are obtained after temperature treatment (eg 200°C for 1 hour)
• The recommended dry film thickness is between 15 and 25μm
Canister 20L
Drum 200L
IBC 1.000L
A&S MP 850 Resin is a solution of methylphenyl silicone resin in xylene.
•Good storage stability when mixed with zinc powder and aluminum pigments
•Easy to use
•Heat stability up to 650°C in combination with aluminum or micaceous iron pigments
Applicable to all types of heat resistant paints. It is the material of choice for anticorrosive coatings in engine parts, furnaces, chimneys, exhaust systems, boilers, ovens and oven parts, grills, electric and gas heaters, incinerators.
For temperatures above 250°C, the organic groups of silicone resins begin to degrade. After all silicone resin organic components have pyrolytically degraded, the remaining product changes to an inorganic stoichiometric composition of (SiO2)n. It is this layer that securely adheres the pigments and fillers to the coated substrate.
Any heat-stable inorganic pigments may be used:
•White, silver, black and colored ones
•Aluminum pigments provide the best heat resistance, up to 600°C
•Black pigments up to 500°C
•Mica and talc can be used as fillers
Recommendations for proper use:
•It is necessary to ensure adequate dispersion of pigments and fillers in the paint
•Sandblasting and degreasing of the substrate are recommended
•The paint can be made by spraying, immersion or brushing
•The product dries completely at room temperature, promoting temporary protection against corrosion
•The optimum mechanical properties and oil resistance are obtained after temperature treatment (eg 200°C for 1 hour)
•The recommended dry film thickness is between 15 and 25μm